stainless steel welding electrode E316-16

1.Stainless steel welding electrode E316-16 2.Dia(mm):2.5,3.2,4.0,5.0 3.OEM Service 4.Free sample 5.factory supply

Stainless Steel welding electrode E316-16

Factory: Shijiazhuang shiqiao electric welding material co., ltd.

Sample supply: free

Oem Service:accept

A202According with GB E316-16Corresponding with AWS  E316-16 Introduction:E316-16  is a kind of low-carbon Cr18Ni12Mo2 stainless steel electrode with lime-titania type coating. Due to Mo added to the weld metal, it has excellent corrosion-resistance, heat-resistance and crack-resistance, especially suitable for chloride ion pitting corrosion-resistance. AC/DC. It has excellent welding performance

Application:

Used for welding 0Cr18Ni12Mo2 stainless steel equipment working in organic acid and mineral acid (non-oxidizing acid) medium, and also used for welding dissimilar steel.

Specification:

Chemical Composition of Deposited Metal (%)

Chemical Composition	C	Mn	Si	S	P	Cu	Ni	Mo	Cr
Guarantee Value	≤0.08	0.5~2.5	≤0.90	≤0.030	≤0.040	≤0.75	11.0~14.0	2.00~3.00	17.0~20.0

Mechanical Properties of Deposited Metal

Test Item	Rm(MPa)	A(%)
Guarantee Value	≥520	≥30

Reference Current(AC, DC+)

Electrode Diameter(mm)	φ2.0	φ2.5	φ3.2	φ4.0	φ5.0
Welding Current (A)	40~80	50~100	70~130	100~160	140~200

Instructions:1.The electrodes should be baked under 200-250°C for an hour before welding.2.Direct current had better be used and the current should not be too strong.

stainless steel welding electrode E316-16